全部

1·Through theory analysis a mathmatical relation between martensitic {112} crystal plane diffraction peak is established.

通过讨论分析，建立了马氏体碳浓度与马氏体{112}晶面族衍射峰双线分离距离之间的关系式。

2·With the increasing of oxygen partial pressure, angle of (002) diffraction peak becomes larger and surface RMS of the films reduces.

随氧分压增加，（002）衍射峰的角度变大，表征薄膜表面粗糙程度的方均根粗糙度减小。

3·XRD analysis is discussed on this system, and a method of calculation content of phase content in by X ray diffraction peak intensity is researched.

并对系统进行了X -射线分析，探讨了用x -射线衍射峰强度计算各物相含量的方法。

4·However, the diffraction peak of the original montmorillonite significantly shifts to small angle, the layer distance increases more than three times.

结果发现，经直接混炼之后，有机蒙脱土的衍射峰向小角度偏移很小，层间距没有明显变化；

5·According to the experimental product derived from its X-ray powder diffraction peak curve bread is amorphous, glycine template no diffraction peak of copper.

根据实验所得的产物其x -射线粉末衍射曲线呈馒头峰是非晶态，没有出现模板甘氨酸铜的衍射峰。

6·The invention provides an amorphous cefodizime sodium, which is characterized in that an amorphous X-ray diffraction pattern is free from having an X-ray diffraction peak;

本发明提供了一种无定形头孢地嗪钠，该无定形的X-射线衍射图中未出现X-射线衍射峰；

7·The XRD characterization shows that the width of XRD diffraction peak gets narrow with the increase of calcined temperature, which indicates the crystallinity has improved.

结果表明，随着焙烧温度的增加XRD衍射峰的宽度逐渐变窄，表明样品的结晶度变好；

8·The low temperature plasma nitrided case of 321 stainless steel was analyzed by XRD, and the analysis found that the diffraction peak had evidently moved in low-angle region.

对经低温离子渗氮的AISI 321纲渗层进行了XRD分析，发现试样的谱峰明显向低角度偏移。

9·This paper describes a processing method for automatically searching peak of X-ray diffraction signal.

介绍了一种对X射线衍射峰信号进行自动判别峰位的数据处理方法。

10·The experimental results show that a bigger diffraction efficiency delay rate can make the establishing time of the laser pulse and the pulse width shorter, and make the peak power higher.

实验结果表明，在一定范围内增大衍射延迟速率可以缩短脉冲建立时间，缩短脉冲宽度，增加峰值功率。