1·Technological essentials for the smelting tool steels with scheelite, molybdenum oxide and vanadium slag are also given in this paper.

并给出了用白钨矿、氧化钼和钒渣冶炼工具钢的工艺要点。

2·The test for producing ferrovanadium-titanium-silicon with un-chemically treated atomized vanadium slag as materials is conducted in Panzhihua I & S Co.

对以攀钢雾化钒渣为原料不经化学处理直接冶炼钒钛硅铁复合合金的试验进行了研究。

3·Smelting reduction process of sheelite, molybdenum oxide and vanadium slag is considered by thermodynamic and kinetic calculation and analysis in the paper.

对用白钨矿、氧化钼和钒渣冶炼高速钢进行热力学和动力学的计算与分析。

4·Smelting tool steels with scheelite, molybdenum oxide and vanadium slag is investigated by thermodynamic and kinetic calculation and analysis in this paper.

对用白钨矿、氧化钼和钒渣冶炼工具钢进行了热力学和动力学计算和分析。

5·The following V2O5 recovery process is directly effected by the quality and the grade of vanadium slag, which is the main raw material to produce vanadium product.

钒渣作为生产钒产品的主要原料，其质量和品位直接影响到后续提取V2O5工艺。

6·It discusses the influences of temperature, the types of sodium salt, and the adding amounts of sodium salt to extracting vanadium pentoxide from high-silicon low-vanadium vanadium slag.

讨论了温度、钠盐种类及钠盐加量对高硅低钒钒渣提取五氧化二钒的影响。

7·Gallium contents in 6 different types of sample including iron, slag, discarded slag after vanadium extraction are determined by this method with analysis accuracy up to requirements.

用该方法测定了铁、渣、浸钒渣等六种不同类型试样中镓的含量，分析其精度符合要求。

8·The behaviour of the vanadium bearing slag in smelting process has been discussed.

讨论了含钒转炉渣在炼钢过程中的行为。

9·The melting temperature and its range of the converter slag containing vanadium and titanium oxides (different contents) were measured.

测定了钒钛钢渣在不同组元含量条件下的熔化性温度及熔化区间。

10·The second step of the pretreatment, the vanadium extraction process in BOF is carried out after slag steelmaking.

脱硫铁水经撇渣后，进行二次预处理，即转炉提钒。