全部

1·The formulation and process of epoxy primer and polyester polyurethane top finish in this system were introduced.

介绍了该涂料体系的环氧底漆和聚酯聚氨酯面漆的配方和生产工艺。

2·This blended and filled the detail repairs as well as the 220 grit surface left in the epoxy primer coat by the blocking process.

在环氧树脂底漆上经过补土程序，添加辅料、填补凹陷后用220号砂纸打磨。

3·We researched the preparation of the magnetism ferric oxide epoxy primer through a serious of experiments, based in consulted information .

通过实验，研究了磁性氧化铁环氧底漆的制备，检测了其各项性能指标。

4·The epoxy primer used in the recoating test was trial-produced and the effect of different content of the PVC on the result of recoating test was examined.

试制了环氧底漆用于复涂实验，考察了不同PVC含量对于复涂实验结果的影响。

5·According to the requirement of coatings, yellow zine epoxy primer and two - pack high solid acrylate polyurethane coating are chosen to be containers paints.

根据涂层的要求，选择了锌黄环氧底漆和双组分高固体丙烯酸聚氨酯漆作为厢体的涂料。

6·Donghua's GH602 Iron-red Epoxy Primer is a two-part amine-adduct cured epoxy primer; and GH102 Ceramic Epoxy Topcoat is a two-part amine-adduct cured epoxy topcoat.

东化公司的GH 602环氧铁红底漆是双组份、胺加成物固化的环氧底漆，GH 102环氧陶瓷面漆是双组份、胺加成物固化的环氧面漆。

7·The result indicated when the epoxy primer in which the content of the PVC was higher than that of the CPVC was recoated, it would cause blistering on the paint film.

结果表明，在PV C含量高于CPVC的环氧底漆上复涂时，会引起所复涂涂料起泡的漆膜缺陷。

8·Blast clean damaged area, previously coated with zinc silicate and prime with a two-pack zinc rich epoxy primer (containing at least 90% by weight of zinc in the dry film).

喷砂清理以前涂有硅酸锌的损坏区域，并涂敷一层双组分环氧富锌底漆(干膜中含有90%重量百分比的锌)。

9·Spraying must be washed clean appearance, there is oily wax with a agent oil, new welding or metal appearance except rust after use of epoxy resin antirust primer to prevent rust.

施喷外表必定要用水洗洁净，有油质，蜡质要用出有剂出油，新焊接或除铁锈后的金属外表要用——环氧树脂防锈底漆处理以防生锈。

10·A reasonable formulation for epoxy zinc-rich shop primer was designed through many experiments, the prepared film property was complyed with national standard, and the paint reduced the pollution.

通过大量的试验研究，设计了一个合理的环氧富锌车间底漆配方，制备出的涂料漆膜性能符合国家标准，且降低了涂料整体的污染程度。