1·And pouring temperature has little effect on modification.

浇铸温度对其变质效果影响不大。

2·The effect of te coating and pouring temperature on chilled layer of cast iron are researched.

研究了碲涂料的组成与浇注温度对激冷层的影响。

3·Proper decrease in pouring temperature and increase in shell mold temperature are helpful to preventing hot tear.

为避免产生热裂应适当降低浇注温度，提高型壳温度。

4·The influence of chemical component. centrifugal time and pouring temperature on roll ring quality has been discussed.

文中叙述了化学成分、离心时间、浇注温度对辊套质量的影响。

5·There exists a critical value for pouring temperature, which is closely related to die temperature and releasing agent.

浇注温度有最佳值，最佳值的大小和模具温度、脱模剂有关。

6·The melting speed, overheat temperature, pouring temperature and modification in production of high chrome cast iron were studied.

对高铬铸铁的熔炼速度、过热温度、浇注温度及变质处理进行了研究。

7·The higher the pouring temperature or the larger the sprue hollow area rate is, the faster the filling velocity of molten aluminum is.

浇注温度越高、直浇道空心面积率越大，铝液充型速度越快。

8·The influence of melting rate, super heating temperature, pouring temperature and modification on high chromium cast iron were researched.

对高铬铸铁的熔炼速度、 过热温度、浇注温度和变质处理进行了研究。

9·The higher the pouring temperature and initial mold temperature are, the larger the plastic strain while the smaller the thermal stress is.

浇注温度和砂型初始温度越高，热节处粘塑性应变越大，而热应力越小。

10·As pouring temperature decreasing, primary phase in the alloy without re addition changes from large dendritic crystal to equiaxed crystal.

未添加re的合金，随浇注温度的下降，其初生相由发达的树枝晶转变成等轴枝晶。